國內(nèi)常用的太陽能晶硅電池片根據(jù)尺寸和單多晶可分為:
單晶125*125
單晶156*156
多晶156*156
單晶150*150
單晶103*103
多晶125*125
技術(shù)參數(shù)
125S晶體硅太陽電池技術(shù)參數(shù)
檔次 | 轉(zhuǎn)換效率 | 功率 | 功率點電流 | 最小功率點電流 | 功率點電壓 | 短路電流 | 開路電壓 |
Pm(Wp) | Im(A)max | Im(A)min | Vm(V) | Isc(A) | Voc(V) | ||
A | 18.00% | 2.674-2.696 | 5.135 | 5.093 | 0.525 | 5.440 | 0.630 |
B | 17.80% | 2.645-2.673 | 5.111 | 5.057 | 0.523 | 5.410 | 0.628 |
C | 17.60% | 2.615-2.644 | 5.075 | 5.019 | 0.521 | 5.380 | 0.627 |
D | 17.45% | 2.593-2.614 | 5.027 | 4.987 | 0.520 | 5.350 | 0.627 |
E | 17.30% | 2.570-2.592 | 5.004 | 4.961 | 0.518 | 5.330 | 0.626 |
F | 17.15% | 2.548-2.569 | 4.988 | 4.948 | 0.515 | 5.320 | 0.620 |
G | 17.00% | 2.526-2.547 | 4.975 | 4.933 | 0.512 | 5.300 | 0.620 |
H | 16.85% | 2.504-2.525 | 4.949 | 4.910 | 0.510 | 5.280 | 0.615 |
I | 16.70% | 2.481-2.503 | 4.956 | 4.913 | 0.505 | 5.260 | 0.615 |
J | 16.50% | 2.452-2.480 | 4.911 | 4.850 | 0.505 | 5.240 | 0.615 |
K | 16.25% | 2.414-2.451 | 4.853 | 4.780 | 0.505 | 5.200 | 0.615 |
L | 16.00% | 2.377-2.413 | 4.778 | 4.707 | 0.505 | 5.160 | 0.610 |
M | 15.75% | 2.340-2.376 | 4.752 | 4.680 | 0.500 | 5.000 | 0.610 |
N | 15.50% | 2.303-2.339 | 4.678 | 4.606 | 0.500 | 4.980 | 0.605 |
O | 15.25% | 2.266-2.302 | 4.604 | 4.578 | 0.495 | 4.960 | 0.605 |
P | 15.00% | 2.229-2.265 | 4.576 | 4.503 | 0.495 | 4.940 | 0.600 |
SF156M多晶體硅太陽電池技術(shù)參數(shù)
檔次 | 轉(zhuǎn)換效率 | 功率 | 功率點電流 | 功率點電壓 | 短路電流 | 開路電壓 |
Pm(Wp) | Im(A) | Vm(mV) | Isc(A) | Voc(mV) | ||
A | 17.50% | 4.258 | 8.189 | 520 | 9.30±5% | 625±5% |
B | 17.25% | 4.198 | 8.072 | 520 | 9.22±5% | 625±5% |
C | 17.00% | 4.137 | 7.955 | 520 | 9.11±5% | 625±5% |
D | 16.75% | 4.076 | 7.914 | 515 | 9.01±5% | 620±5% |
E | 16.50% | 4.015 | 7.796 | 515 | 8.89±5% | 620±5% |
F | 16.25% | 3.954 | 7.678 | 515 | 8.78±5% | 620±5% |
G | 16.00% | 3.893 | 7.560 | 515 | 8.67±5% | 620±5% |
H | 15.75% | 3.833 | 7.515 | 510 | 8.56±5% | 615±5% |
I | 15.50% | 3.772 | 7.396 | 510 | 8.45±5% | 615±5% |
J | 15.25% | 3.711 | 7.348 | 505 | 8.30±5% | 615±5% |
K | 15.00% | 3.650 | 7.228 | 505 | 8.16±5% | 615±5% |
L | 14.75% | 3.589 | 7.107 | 505 | 8.01±5% | 615±5% |
M | 14.50% | 3.528 | 6.987 | 505 | 7.87±5% | 615±5% |
N | 14.25% | 3.468 | 6.935 | 500 | 7.75±5% | 610±5% |
O | 14.00% | 3.407 | 6.814 | 500 | 7.61±5% | 610±5% |
P | 13.50% | 3.285 | 6.637 | 495 | 7.38±5% | 610±5% |
Q | 13.00% | 3.163 | 6.456 | 490 | 7.12±5% | 610±5% |
R | 12.50% | 3.042 | 6.272 | 485 | 7.86±5% | 610±5% |
S | 12.00% | 2.920 | 6.084 | 480 | 6.56±5% | 605±5% |
T | 11.50% | 2.798 | 5.891 | 475 | 6.34±5% | 600±5% |
U | 11.00% | 2.677 | 5.695 | 470 | 6.08±5% | 590±5% |
V | 10.50% | 2.555 | 5.495 | 465 | 5.82±5% | 580±5% |
W | <10.5% |
相關(guān)組件
125*125單晶
晶體硅太陽電池的優(yōu)良性能簡介:
·高效率,低衰減,可靠性強;
·*的擴散技術(shù),保證了片間片內(nèi)的良好均勻性,降低了電池片之間的匹配損失;
·運用*的管式PECVD成膜技術(shù),使得覆蓋在電池表面的深藍色氮化硅減反射膜致密、均勻、美觀;
·應用高品質(zhì)的金屬漿料制作電極和背場。確保了電極良好的導電性、可焊性以及背場的平整性;
·高精度的絲網(wǎng)印刷圖形,使得電池片易于自動焊接。
156*156多晶
晶體硅太陽電池的優(yōu)良性能簡介:
除了125*125單晶電池的優(yōu)良性能外還有以下性能
·高精度的絲網(wǎng)印刷圖形,使得電池片易于自動焊接。
125單晶
晶體硅太陽能電池組件的優(yōu)良性能簡介:
·SF-PV的組件可以滿足不同的消費層次
·使用高效率的硅太陽能電池
·組件標稱電壓24/12V DC
·3.2mm厚的鋼化玻璃
·為提高抗風能力和抗積雪壓力,使用耐用的鋁合金框架以方便裝配,
·組件邊框設計有用于排水的漏水孔消除了在冬天雨或雪水長期積累在框架內(nèi)造成結(jié)冰甚至使框架變形
·電纜線使用快速連接頭來裝配
·滿足顧客要求的包裝
·保證25年的使用年限
156多晶
晶體硅太陽能電池組件的優(yōu)良性能簡介:同125單晶的優(yōu)良性能
制造工藝
太陽能電池片的生產(chǎn)工藝流程分為硅片檢測——表面制絨及酸洗——擴散制結(jié)——去磷硅玻璃——等離子刻蝕及酸洗——鍍減反射膜——絲網(wǎng)印刷——快速燒結(jié)等。
太陽能電池片網(wǎng)狀隱裂
原因
1.電池片在焊接或搬運過程中受外力造成.
2.電池片在低溫下沒有經(jīng)過預熱在短時間內(nèi)突然受到高溫后出現(xiàn)膨脹造成隱裂現(xiàn)象
組件影響
1.網(wǎng)狀隱裂會影響組件功率衰減.
2.網(wǎng)狀隱裂長時間出現(xiàn)碎片,出現(xiàn)熱斑等直接影響組件性能
預防措施
1.在生產(chǎn)過程中避免電池片過于受到外力碰撞.
2.在焊接過程中電池片要提前保溫(手焊)烙鐵溫度要 符合要求.
3.EL測試要嚴格要求檢驗.