一、產(chǎn)品簡(jiǎn)介：
渣球含量測(cè)定儀是檢測(cè)儀器，可對(duì)玻璃棉及其制品，礦渣棉、巖棉、及其制品，硅酸鋁棉及其制品進(jìn)行渣球含量進(jìn)行分析。
Product introduction:
The slag ball content tester is a testing instrument that can analyze the slag ball content of glass wool and its products, slag wool, rock wool and its products, aluminum silicate cotton and its products.
二、技術(shù)參數(shù)：
★玻璃轉(zhuǎn)子流量計(jì)：0-200mL/min
★分離筒：內(nèi)徑80mm高380mm
★纖維收集器：138x98mm
★渣球收集器：138x98mm
★塑料水槽：210x140mm
★外形尺寸：390x185x570mm
★重量：15kg
Technical parameters:
★ Glass rotor flowmeter: 0-200mL / min
★ Separation tube: 80mm inner diameter and 380mm high
★ Fiber collector: 138x98mm
★ Grit ball collector: 138x98mm
★ Plastic sink: 210x140mm
★ Dimensions: 390x185x570mm
★ Weight: 15kg
三、使用方法：
1，制備試樣
按GB/T5480.5-2004的規(guī)定選取式樣，切取全厚度的試樣11g左右。在對(duì)于玻璃棉及其制品，在（500±20）℃下灼燒30min以上；對(duì)于硅酸棉及其制品，在（700±20）℃下灼燒30min以上。除盡粘結(jié)劑再稱量**到0.01g。試樣數(shù)量按產(chǎn)品標(biāo)準(zhǔn)的規(guī)定，但不應(yīng)少于3個(gè)。
2，壓制試樣
把稱量好的試樣放入相應(yīng)的試樣筒內(nèi)，放于壓榨器上進(jìn)行手動(dòng)螺旋加壓。
3，潤(rùn)濕試樣
將壓制好的試樣取出，放于250mL量杯內(nèi)，加入表面活性劑溶液50mL，并充分?jǐn)嚢瑁估w維在溶液中得到潤(rùn)濕和分散。
4，分離試驗(yàn)
?將試樣全部移入分離筒中。
?打開(kāi)水源開(kāi)關(guān)，使轉(zhuǎn)子流量計(jì)的流量示值為60mL/min，保持此流量直至纖維在水中得到分散和懸浮。
?加大水流量至（120-180）mL/min，繼續(xù)分離10min左右。
?待分離筒內(nèi)水澄清后，打開(kāi)分離筒下端的排渣閥，借助水流把渣球排入邊長(zhǎng)不大于產(chǎn)品標(biāo)準(zhǔn)規(guī)定的篩孔邊長(zhǎng)的標(biāo)準(zhǔn)篩內(nèi)。
?檢查纖維收集器內(nèi)的纖維中是否含有渣球，若有渣球應(yīng)將其放入分離器內(nèi)在進(jìn)行分離。
5，干燥
將盛有渣球的篩子放入電熱干燥箱內(nèi)，在（105-110）℃溫度下烘干至少20min。
6，篩分
將干燥的渣球移入產(chǎn)品標(biāo)準(zhǔn)規(guī)定的篩孔的標(biāo)準(zhǔn)篩內(nèi)，加入3只直徑為（20±1）mm的陶瓷球，蓋裝后啟動(dòng)振篩機(jī)篩分15min。
7，稱量
將篩分后的渣球放在天平上稱重，讀數(shù)**到0.01g。
8，計(jì)算
渣球含量sｈ-按下式計(jì)算：
Sh=m/moX100
式中：
sｈ—渣球含量，單位為百分?jǐn)?shù)（％）；
m—渣球質(zhì)量，單位為克（g）。
m0-試樣質(zhì)量，單位為克（g）。
9，試驗(yàn)結(jié)果
試驗(yàn)結(jié)果以算術(shù)平均值表示，**到小數(shù)點(diǎn)后A位。同時(shí)報(bào)出所有篩孔的孔徑。
實(shí)驗(yàn)完畢后清理好以便下次使用.
Third, use method:
1. Prepare the sample
Select the pattern according to GB / T5480.5-2004, and cut about 11g of the full thickness sample. For glass wool and its products, it is fired at (500 ± 20) ℃ for more than 30min; for silicic acid wool and its products, it is fired at (700 ± 20) ℃ for more than 30min. Remove the binder and weigh ** to 0.01g. The number of samples shall be as specified in the product standard, but shall not be less than three.
2. Pressed sample
Put the weighed sample into the corresponding sample tube, put it on the squeezer and perform manual spiral pressure.
3. Wetting the sample
The pressed sample was taken out, placed in a 250 mL measuring cup, and 50 mL of a surfactant solution was added, and thoroughly stirred to make the fibers wet and dispersed in the solution.
4. Separation test
? Move all the samples into the separation cylinder.
? Turn on the water source switch and make the flowmeter display value of the rotor flowmeter 60mL / min. Keep this flowrate until the fibers are dispersed and suspended in the water.
? Increase the water flow to (120-180) mL / min, and continue to separate for about 10 minutes.
? After the water in the separation cylinder is clarified, open the slag discharge valve at the lower end of the separation cylinder and use the water flow to completely discharge the slag ball into a standard sieve whose side length is not greater than the sieve hole side length specified in the product standard.
? Check whether there are slag balls in the fiber in the fiber collector. If there are slag balls, put them in the separator to separate them.
5, dry
Place the slag ball-containing sieve in an electric drying box and dry it at (105-110) ° C for at least 20 minutes.
6. Screening
Move the dried slag ball into the standard sieve of the sieve hole specified in the product standard, add 3 ceramic balls with a diameter of (20 ± 1) mm, and start the vibrating screen for 15 minutes after capping.
7, weighing
The sieved slag ball was weighed on a balance, and the reading was ** to 0.01g.
8. Calculation
The slag ball content sh-calculated as follows:
Sh = m / moX100
In the formula:
sh—slag content, unit is percentage (%);
m—mass of slag ball, unit is gram (g).
m0-sample mass in grams (g).
9. Test results
The test results are expressed as arithmetic mean, ** to the decimal place. At the same time report the pore size of all sieve holes.
Clean up after the experiment for next use.
四、產(chǎn)品結(jié)構(gòu)：
1.分離裝置:包括<0~200) mL/min玻璃轉(zhuǎn)子流量計(jì)；內(nèi)徑為80 mm,總高度為380mm的分離簡(jiǎn);塑料水槽;纖維收集器和渣球收集器等。見(jiàn)圖10。
Product structure:
1. Separation device: Including <0 ~ 200) mL / min glass rotor flowmeter; Separation element with an inner diameter of 80 mm and a total height of 380mm; plastic water tank; fiber collector and ball collector See Figure 10.
2.取樣器:內(nèi)徑為14mm的圓簡(jiǎn)形切取試樣的工具。
3.壓樣設(shè)備:由試樣筒、壓樣筒和壓榨器組成。見(jiàn)圖11。
注1：試樣簡(jiǎn)內(nèi)徑為27mm.有效高度為53.5mm。
注2：壓樣簡(jiǎn)外徑為26mm.有效高度分二種,巖棉、礦渣棉和硅酸鋁棉試驗(yàn)用的為38.2mm;而玻璃棉試驗(yàn)用的為36.2 mm。
2. Sampler: A simple tool for cutting specimens with a circular diameter of 14mm.
3. Sample pressing device: It consists of sample tube, sample tube and press. See Figure 11.
Note 1: The simple inner diameter of the sample is 27mm. The effective height is 53.5mm.
Note 2: The outer diameter of the compressed sample is 26mm. The effective height is divided into two types. The test for rock wool, slag cotton and aluminosilicate cotton is 38.2mm; the test for glass wool is 36.2mm.
4.篩分裝置：包括振篩機(jī)和標(biāo)準(zhǔn)篩。振篩機(jī)振動(dòng)頻率為23.5次/s。
5.天平:A大稱量200 g,分度值小于等于0.01 g。
6.電熱干燥箱:控溫精度為士5C。
7.高溫電爐:可調(diào)節(jié)、控溫精度為士10C。
8.定時(shí)器。